Products - Apus Reacted Zinc
» Back to Products 
DESCRIPTION :
  • Zinc stays in solution once stirred.
  • Extremely easy to apply and easy to recoat.
  • Single component, Apus Reacted urethane.
  • Very resistant to mud cracking.
  • Zinc - rich primer / top coat
  • Recommended for immersion applications when top coated.
  • Colour: Grey
  • High solids, VOC compliant coating.
 
USES:
  • High performance zinc - rich primer or single protective coating in any use on steel where maximum resistance to rust or corrosion undercutting is required.
  • Proven performance as primer in long life, high durability urethane systems for tanks, chemical and marine structures and bridges.
  • Best possible zinc - rich coating for use in Field applications where weather limits the use of other zinc coatings.
 
TECHNICAL DATA :
 
Solids by volume : 62.0 + 2.0%
Weight / Ltr : 2.44 + 0.36 Kg / Ltr
Pigment type : 83 % zinc in Dry film
Flash Point :

Above 40° C

Theoretical coverage : 7 m2 / Ltr @    75 microns
Recommended Dry film thickness :

60 - 75 microns DFT

Temperature  resistance (Dry )  : 150°  C continuous  and   175°  C  intermittent
Curing time @ 25° C : Touch 20 min; Handle - 8 hour ; Recoat - 4 hours; Stack -10 hours
Recoatability :

Tack free ( this is achieved normally in 4 hours )

Colour : Grey
Finish : Matt
Shelf life   :

12 Months  in an  unopened original container.

 
ADVANTAGES :
  • Single component
  • Can be applied in cold, damp conditions at humidities to 99%
  • Can be applied at low temperature to below freezing.
  • Best corrosion resistance to all zinc primers when top coated.
  • Out performs inorganic zinc three coat systems.
 
Products
Coatings for Steel Strappings
Polyurethane Coatings
Apus Reacted Urethanes (ARU)
Polyurethane adhesives (glue)
Polyurethane rigid foam (PUF)
Isocyanate & Isocynurate foams
Water based PU wood lacquers
Coatings for Telecom Towers
 
  Designed and Developed byAster Infotech